Journal of Materials Science

, Volume 30, Issue 11, pp 2738–2742 | Cite as

Reordering, recrystallization and recovery behaviour of (Co0.78Fe0.22)3 V as a function of the initial state of order

Part II Microstructure
  • Y. Lin
  • S. Gialanella
  • R. W. Cahn
Papers
  • 30 Downloads

Abstract

Optical and electron micrography were used to examine the progress of recovery and recrystallization in the (Co-Fe-V) alloy rolled in the initially disordered state and annealed at a range of temperatures, and the results were related to the measurements reported in Part I of this study. The indirect results include a plot of fraction recrystallized at various temperatures against annealing time: unexplained anomalous behaviour was found at the highest temperature. Stacking-faults and antiphase domain boundaries in the recrystallized grains were examined.

Keywords

Polymer Recrystallization Electron Micrography Material Processing Domain Boundary 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    S. Gialanella, R. W. Cahn, M. D. Baró, J. Malagelada, S. Suriñach, J. Soltys, R. Kozubski and W. Wronka, J. Mater. Sci. 28 (1993) 538.CrossRefGoogle Scholar
  2. 2.
    R. W. Cahn, M. Takeyama, J. A. Horton and C. T. Liu, J. Mater. Res. 6 (1990) 57.CrossRefGoogle Scholar
  3. 3.
    D. N. Braski, R. W. Carpenter and J. Bentley, Acta Metall. 30 (1982) 799.CrossRefGoogle Scholar
  4. 4.
    T. Takasugi and O. Izumi, ibid. 33 (1985) 49.CrossRefGoogle Scholar
  5. 5.
    R. A. Buckley, Met. Sci. 13 (1979) 67.CrossRefGoogle Scholar
  6. 6.
    M. Raikovic and R. A. Buckley, ibid. 15 (1981) 21.CrossRefGoogle Scholar
  7. 7.
    L. E. Tanner and H. J. Leamy, in “Order-disorder transformations in alloys”, edited by H. Warlimont (Springer, Heidelberg, 1974) p. 181.Google Scholar
  8. 8.
    R. W. Cahn, in High Temperature Aluminides and Intermetallics”, edited by S. H. Whang, C. T. Liu, D. P. Pope and J. O. Stiegler (TMS, Warrendale, PA, 1990) p. 245.Google Scholar
  9. 9.
    D. P. Pope and S. S. Ezz, Int. Metall Rev. 29 (1984) 136.CrossRefGoogle Scholar

Copyright information

© Chapman & Hall 1995

Authors and Affiliations

  • Y. Lin
    • 1
  • S. Gialanella
    • 1
  • R. W. Cahn
    • 1
  1. 1.Department of Materials Science and MetallurgyUniversity of CambridgeCambridgeUK

Personalised recommendations